Influence of Welding on Dynamic Fracture Toughness of Strenx 700MC Steel

Článekpeer-reviewedsubmitted version
Náhled

Datum publikování

2019

Vedoucí práce

Oponent

Název časopisu

Název svazku

Vydavatel

MDPI AG (Multidisciplinary Digital Publishing Institute)

Abstrakt

Thermomechanically processed high-strength steels feature specific fracture behavior. One of the decisive criteria for their application is their stability against internal defects during impact loads, especially in connection with the welding. The work is focused on experimental analyses of the influence of welding on static and dynamic fracture toughness of Strenx 700MC steel. The fracture toughness was determined using the circumferentially notched round bar specimens during static loads and two dynamic load levels. To achieve a homogeneous zone for the requirements of fracture toughness tests, simulation of the welding influence was performed. Fractographic and metallographic analyses described a specific fracture behavior controlled by the internal structural heterogeneity. A limiting degradation process due to welding was identified by the microstructural analysis.

Rozsah stran

ISSN

2075-4701

Trvalý odkaz na tento záznam

Projekt

TE01020038/Centrum kompetence drážních vozidel

Zdrojový dokument

Metals, volume 9, issue: 5

Vydavatelská verze

https://doi.org/10.3390/met9050494

Přístup k e-verzi

open access
https://creativecommons.org/licenses/by/4.0/

Název akce

ISBN

Studijní obor

Studijní program

Signatura tištěné verze

Umístění tištěné verze

Přístup k tištěné verzi

Klíčová slova

dynamic fracture toughness, high strength steels, fracture behavior, welding influence, heat-affected zone, simulation of welding, heterogeneous carbide precipitation, dynamická lomová houževnatost, vysokopevné oceli, lomové chování, vliv svařování, heterogenní precipitace karbidů

Endorsement

Review

item.page.supplemented

item.page.referenced