SiO2 Fibers by Centrifugal Spinning with Excellent Textural Properties and Water Adsorption Performance
Článekpeer-reviewedpostprint Náhled není k dispozici
Datum publikování
2017
Vedoucí práce
Oponent
Název časopisu
Název svazku
Vydavatel
American Chemical Society
Abstrakt
Facile and innovative route for large-scale synthesis of SiO2 fibers with excellent textural properties and H2O adsorption performance is presented. At first, a three-dimensional network of SiO2 precursor fibers was produced from tailored spun solutions (without any toxic elements and surfactants) by centrifugal spinning, which is a very modern fiber-synthesis technique, with numerous advantages over electrospinning. Upon thermal annealing of the precursor fibers, mesoporous amorphous SiO2 fibers with an ultrahigh surface area of up to 824 m(2)/g and pore size distribution in the range of 2-10 nm were produced. Owing to the high number of OH groups available on the surface, the produced SiO2 fibers showed significantly better performance in H2O adsorption compared to that of the reference silicagel.
Rozsah stran
p. 5052-5059
ISSN
2470-1343
Trvalý odkaz na tento záznam
Projekt
Zdrojový dokument
ACS Omega, volume 2, issue: 8
Vydavatelská verze
Přístup k e-verzi
open access
Název akce
ISBN
Studijní obor
Studijní program
Signatura tištěné verze
Umístění tištěné verze
Přístup k tištěné verzi
Klíčová slova
silica nanofibers, electrospun nanofibers, governing parameters, pressurized gyration, composite, gel, nanoparticles, desiccant, membranes, diameter, adsorpce, desorpce, distribuční funkce, vlákna, tepelný výpal, mikrostruktura, porozita, povrchová struktura