SPECIFIKA HODNOCENÍ OPOTŘEBENÍ V REŽIMU KONTAKTNĚ-ÚNAVOVÉHO ZATĚŽOVÁNÍ

Show simple item record

dc.contributor.author Schmidová, Eva cze
dc.contributor.author Culek, Bohumil cze
dc.contributor.author Kaya, Utku cze
dc.date.accessioned 2017-05-11T10:50:46Z
dc.date.available 2017-05-11T10:50:46Z
dc.date.issued 2016 cze
dc.identifier.isbn 978-80-905947-2-2 cze
dc.identifier.issn cze
dc.identifier.uri http://hdl.handle.net/10195/67328
dc.description.abstract Článek je věnován analýze specifického degradačního mechanizmu kolejnicových ocelí - kumulativnímu vyčerpání plasticity v kombinaci s adhesivním opotřebením. Provozní poškozování kontaktní únavou bylo simulováno použitím specielního zkušebního stendu. cze
dc.format p. 15-21 cze
dc.language.iso cze cze
dc.publisher Flash Steel Power, a.s. cze
dc.relation.ispartof PROMATTEN 2016 cze
dc.rights Pouze v rámci univerzity cze
dc.subject kolejnicová ocel cze
dc.subject kontaktní únava cze
dc.subject opotřebení cze
dc.subject Railway steel eng
dc.subject Contact-Fatigue eng
dc.subject Wearing eng
dc.title SPECIFIKA HODNOCENÍ OPOTŘEBENÍ V REŽIMU KONTAKTNĚ-ÚNAVOVÉHO ZATĚŽOVÁNÍ cze
dc.title.alternative Specifics Evaluation of the Contact-Fatigue Wearing eng
dc.type ConferenceObject cze
dc.description.abstract-translated Railway steels are subjected to specific degradation mechanism due to combination of rolling contact loading and adhesive wearing. Precise evaluation of the surface layer's mechanical parameters is necessary for a service life prediction. Very low depth of localized dislocation hardening process doesn´t allow the standard mechanical testing. The operational degradation of surface layers due to a rolling contact process was simulated by a special testing rig. In the presented study, the rolling contact fatigue resistance of Hadfield steel was tested in two states – with and without explosive hardening. A specific limited state based on cumulative depletion of plasticity was achieved. Adhesive resistance of weld deposits was evaluated as an estimation of the operational durability of selected renovation technologies. eng
dc.event PROMATTEN 2016 (10.11.2016 - 11.11.2016) cze
dc.peerreviewed yes cze
dc.publicationstatus postprint cze
dc.identifier.obd 39878042 cze


This item appears in the following Collection(s)

Show simple item record

Search DSpace


Advanced Search

Browse

My Account