Waterborne coatings based on acrylic latex containing nanostructured ZnO as an active additive
Článekpeer-reviewedpostprintDatum publikování
2020
Vedoucí práce
Oponent
Název časopisu
Název svazku
Vydavatel
Springer
Abstrakt
This work was devoted to the study of the properties of an acrylate latex-based binder synthesized by semicontinuous emulsion polymerization. Nanoparticles of zinc oxide (NPsZnO) in an amount of 1.5 wt% with respect to the polymer content were added to the binder during the synthesis procedure. The binder was then homogenized with various anticorrosion pigments, fillers, and additives to obtain model anticorrosion paints. In addition, model paints with expected enhanced antimicrobial resistance designed for the protection of mineral substrates were also formulated and prepared. The effects of NPsZnO on the physicomechanical properties and on the chemical, anticorrosion, and antimicrobial resistance of the paint films were examined. The properties of the paints based on the synthesized binders were also compared to those of a commercial acrylate-type binder. The results show that incorporation of NPsZnO into the latex during the synthesis provided stable polymeric dispersions exhibiting physicochemical, mechanical, and anticorrosion properties that were superior to those of a blank binder (containing no nanoparticles) as well as to the commercial binder. It was also demonstrated that the binder with NPsZnO provided anticorrosion paints that are usable as coatings for environments with a moderate corrosion burden as well as paints for interior applications with reduced biocide contents.
Rozsah stran
p. 517-529
ISSN
1547-0091
Trvalý odkaz na tento záznam
Projekt
Zdrojový dokument
Journal of Coatings Technology and research, volume 17, issue: 2
Vydavatelská verze
https://link.springer.com/article/10.1007/s11998-019-00302-6
Přístup k e-verzi
open access (CC BY-NC-ND 4.0)
Název akce
ISBN
Studijní obor
Studijní program
Signatura tištěné verze
Umístění tištěné verze
Přístup k tištěné verzi
Klíčová slova
acrylic latex, antimicrobial coating, flash rust, zinc oxide nanoparticle, anticorrosion coating, akrylový latex, antimikrobiální povlak, blesková koroze, nanočástice oxidu zinečnatého, antikorozní povlak