Raman spectroscopy study of glass corrosion
Článekpeer-reviewedpreprint (submitted version) Náhled není k dispozici
Soubory
Datum publikování
2020
Vedoucí práce
Oponent
Název časopisu
Název svazku
Vydavatel
Elsevier Science BV
Abstrakt
Binary sodium silicate and potassium silicate glasses with different alkali content were exposed to the corrosion environment of 35 % hydrochloric acid (HCl). Glass samples were measured by Raman spectroscopy and the spectra were compared with Raman spectra of original pristine glasses in order to observe structural changes induced by corrosion within the surface layer. The usage of confocal Raman spectroscope enabled the measurement of Raman spectra from the depths of few micrometres to document the range of structural changes. The results suggest the depolymerisation of silicate structure due to the growth of the corrosion layer on the surface. The decrease of D2 peak points at the decomposition of three-membered rings. In addition, it is assumed that the Si-O-Si angle changes within the surface layer.
Rozsah stran
"103096-1"-"103096-8"
ISSN
0924-2031
Trvalý odkaz na tento záznam
Projekt
Zdrojový dokument
Vibrational Spectroscopy, volume 109, issue: July
Vydavatelská verze
https://www.sciencedirect.com/science/article/pii/S0924203120300990?via%3Dihub
Přístup k e-verzi
bez omezení
Název akce
ISBN
Studijní obor
Studijní program
Signatura tištěné verze
Umístění tištěné verze
Přístup k tištěné verzi
Klíčová slova
alkali silicate glass, Raman spectroscopy, corrosion, glass surface, glass structure, silikátová skla, Ramanova spektroskopie, koroze, skelný povrch, skelná struktura