dc.description.abstract |
V diplomové práci byla připravena nová borofosfátová skla barnatá modifikovaná přídavky oxidu molybdenového a wolframového. Skla byla studována v kompozičních řadách (100-x)[0,5BaO-0,1B2O3-0,4P2O5]-xMoO3 (řada A) a (100-x)[0,5BaO-0,1B2O3-0,4P2O5]-xWO3 (řada C). V obou systémech se podařilo získat homogenní skelné vzorky s obsahem 0-60 mol. % MoO3 i WO3. Dále byla připravena skla v kompozičních řadách 40BaO-yB2O3-(40-y)P2O5-MoO3 (řada B) a 40BaO-yB2O3-(40-y)P2O5-20WO3 (řada D) s obsahem y = 0-12 mol.% B2O3. |
cze |
dc.format |
93 s. |
|
dc.language.iso |
cze |
|
dc.publisher |
Univerzita Pardubice |
cze |
dc.rights |
bez omezení |
cze |
dc.subject |
borofosfátová skla |
cze |
dc.subject |
termická analýza |
cze |
dc.subject |
NMR spektroskopie |
cze |
dc.subject |
rentgenová difrakční analýza |
cze |
dc.subject |
ramanova spektroskopie |
cze |
dc.subject |
borophosphate glasses |
eng |
dc.subject |
thermal analysis |
eng |
dc.subject |
NMR spectroscopy |
eng |
dc.subject |
x-ray diffraction analysis |
eng |
dc.subject |
raman spectroscopy |
eng |
dc.title |
Borofosfátová skla barnatá modifikovaná oxidem molybdenovým a wolframovým |
cze |
dc.title.alternative |
Barium borophosphate glasses modified with molybdenum oxide and tungsten oxide |
eng |
dc.type |
diplomová práce |
cze |
dc.contributor.referee |
Vlček, Milan |
|
dc.date.accepted |
2019-06-03 |
|
dc.description.abstract-translated |
In this thesis new barium borophosphate glasses modified with molybdenum oxide and tungsten oxide were prepared and studied. Basic glass series have the following composition: (100-x)[0,5BaO-0,1B2O3-0,4P2O5]-xMoO3 (series A) and (100-x)[0,5BaO-0,1B2O3-0,4P2O5]-xWO3 (series C). Homogenous glass samples were obtained in a broad compositional range with 0-60 mol% MoO3 or WO3. Another two compositional series were prepared with a constant content of 20 mol% of the modifying oxides MoO3 (WO3): 40BaO-yB2O3-(40-y)P2O5-MoO3 (series B) and 40BaO-yB2O3-(40-y)P2O5-20WO3 (series D) with y = 0-12 mol.% B2O3. |
eng |
dc.description.department |
Fakulta chemicko-technologická |
cze |
dc.thesis.degree-discipline |
Materiálové inženýrství |
cze |
dc.thesis.degree-name |
Ing. |
|
dc.thesis.degree-grantor |
Univerzita Pardubice. Fakulta chemicko-technologická |
cze |
dc.identifier.signature |
D39334 |
|
dc.thesis.degree-program |
Chemie a technologie materiálů |
cze |
dc.description.defence |
Diplomant seznámil komisi se svojí diplomovou prací.
Dále reagoval na připomínky oponenta.
Zodpověděl otázky členů komise:
Diskutujte pojem izolovaný oktaedr MoO6.
Diskutujte NMR měření.
Upřesněte prezentované DTA křivky. |