dc.description.abstract |
Byla připravena skla systému xMnO-(50-x)ZnO-50P2O5 (1); xSb2O3-(50-2x)ZnO-(50+x)P2O5(2); xMoO3-(50-2x)ZnO-(50+x)P2O5 (3). Pro skla systému (1) byla stanovena měrná hmotnost a molární objem, teplotou skelné transformace, deformační teplotou měknutí, koeficientem teplotní roztažnosti a stabilita podchlazených tavenin. Skla byla dále charakterizována měřením teplotní závislosti stejnosměrné elektrické vodivosti. Struktura látek byla ověřena Ramanovou spektroskopií a elektronovou paramagnetickou rezonancí. |
cze |
dc.format |
71 s. |
cze |
dc.format.extent |
248765 bytes |
cze |
dc.format.mimetype |
application/pdf |
cze |
dc.language.iso |
cze |
|
dc.publisher |
Univerzita Pardubice |
cze |
dc.rights |
Práce není přístupná |
cze |
dc.subject |
metafosforečnanová skla |
cze |
dc.subject |
struktura a vlastnosti skel |
cze |
dc.subject |
termomechanická analýza |
cze |
dc.subject |
stejnosměrná elektrická vodivost |
cze |
dc.subject |
ramanova spektroskopie |
cze |
dc.title |
Metafosforečnanová skla kovů různého mocenství |
cze |
dc.title.alternative |
Metaphosphate glasses of metals of different valence |
eng |
dc.type |
diplomová práce |
cze |
dc.contributor.referee |
Černošková, Eva |
|
dc.date.accepted |
2014 |
cze |
dc.description.abstract-translated |
In the thesis the glass compositional range xMnO- (50-x) ZnO-50P2O5 where x = 0, 2, 5, 10, 15, 20, 30, 40 and 50 has been studied. There were thus prepared a total of nine samples of glass. Basic glass 50ZnO-50P2O5 was colorless, the glass containing MnO was tinged with violet color. Glasses in its entire compositional range were clear, without the presence of crystalline phases. Using magnetic susceptibility it has been found that under the sensitivity of the method (? 1%), the manganese located in the glass as divalent. The violet color of the glass, however, indicates the presence of Mn3+ ions, which was confirmed by electron absorption spectroscopy in the ultraviolet and visible region, when in the spectral glasses containing MnO a wide absorption band was identified consisting of electron transitions Mn3+, which are responsible for the purple color of the glass. |
eng |
dc.description.department |
Katedra obecné a anorganické chemie |
cze |
dc.thesis.degree-discipline |
Materiálové inženýrství |
cze |
dc.thesis.degree-name |
Ing. |
cze |
dc.thesis.degree-grantor |
Univerzita Pardubice. Fakulta chemicko-technologická |
cze |
dc.identifier.signature |
D31634 |
cze |
dc.thesis.degree-program |
Chemie a technologie materiálů |
cze |
dc.rights.physicalunit |
práce není přístupná |
cze |
dc.description.defence |
Diplomant seznámil komisi se svojí diplomovou prací.
Dále reagoval na připomínky oponenta.
Zodpověděl otázky členů komise:
Upřesněte z jakých veličin bylo stanoveno Hrubého kritérium.
Jakou metodou byly stanoveny teploty tání.
Který vzorek je dle Hrubého kritéria nejstabilnější?
Upřesněte stabilitu studovaných skel.
Vysvětlete zvýšení hustoty studovaných skel s rostoucí koncentrací MnO.
Vysvětlete měření volt-ampérové charakteristiky u stejnosměrné elektrické vodivosti. |