Rolling-Contact Hardening Evaluated by Indentation

Konferenční objektOmezený přístuppeer-reviewedpostprint
Náhled

Datum publikování

2016

Autoři

Schmidová, Eva
Kaya, Utku
Schmid, Michal
Culek, Bohumil

Vedoucí práce

Oponent

Název časopisu

Název svazku

Vydavatel

Trans Tech Publications

Abstrakt

The operational degradation of surface layers due to a rolling contact process was simulated for Hadfield steel by a special testing rig. A specific limited state based on cumulative depletion of plasticity was achieved. Precise evaluation of the surface layer's mechanical parameters is necessary for a service life prediction. Very low depth of localized dislocation hardening process doesn´t allow the standard mechanical testing. The comparative instrumented indentation tests using Vickers and cylindrical indenter were used for evaluation of defined stage of surface degradation process. The intensity and reach of deformation hardening are partially limiting for particular methodology. The yield stress of surface layers was estimated according to an analytical model of uniaxial vs. indentation plastic flow ratio.

Rozsah stran

p. 11-14

ISSN

1012-0386

Trvalý odkaz na tento záznam

Projekt

TE01020038/Centrum kompetence drážních vozidel

Zdrojový dokument

Defect and Diffusion Forum

Vydavatelská verze

Přístup k e-verzi

Pouze v rámci univerzity

Název akce

12th International Conference Local Mechanical Properties (04.11.2015 - 06.11.2015)

ISBN

978-3-03835-720-9

Studijní obor

Studijní program

Signatura tištěné verze

Umístění tištěné verze

Přístup k tištěné verzi

Klíčová slova

rolling contact fatigue, Hadfield steel, cylindrical indentation, kontaktní únava, Hadfieldova ocel, válcová indentace

Endorsement

Review

item.page.supplemented

item.page.referenced