SPECIFIKA HODNOCENÍ OPOTŘEBENÍ V REŽIMU KONTAKTNĚ-ÚNAVOVÉHO ZATĚŽOVÁNÍ

Schmidová, Eva; Culek, Bohumil; Kaya, Utku

Digitální knihovna UPCE
→
Univerzita Pardubice
→
Publikační činnost akademických pracovníků UPCE / UPCE Research Outputs
→
Zobrazit záznam

dc.contributor.author	Schmidová, Eva	cze
dc.contributor.author	Culek, Bohumil	cze
dc.contributor.author	Kaya, Utku	cze
dc.date.accessioned	2017-05-11T10:50:46Z
dc.date.available	2017-05-11T10:50:46Z
dc.date.issued	2016	cze
dc.identifier.isbn	978-80-905947-2-2	cze
dc.identifier.issn		cze
dc.identifier.uri	http://hdl.handle.net/10195/67328
dc.description.abstract	Článek je věnován analýze specifického degradačního mechanizmu kolejnicových ocelí - kumulativnímu vyčerpání plasticity v kombinaci s adhesivním opotřebením. Provozní poškozování kontaktní únavou bylo simulováno použitím specielního zkušebního stendu.	cze
dc.format	p. 15-21	cze
dc.language.iso	cze	cze
dc.publisher	Flash Steel Power, a.s.	cze
dc.relation.ispartof	PROMATTEN 2016	cze
dc.rights	Pouze v rámci univerzity	cze
dc.subject	kolejnicová ocel	cze
dc.subject	kontaktní únava	cze
dc.subject	opotřebení	cze
dc.subject	Railway steel	eng
dc.subject	Contact-Fatigue	eng
dc.subject	Wearing	eng
dc.title	SPECIFIKA HODNOCENÍ OPOTŘEBENÍ V REŽIMU KONTAKTNĚ-ÚNAVOVÉHO ZATĚŽOVÁNÍ	cze
dc.title.alternative	Specifics Evaluation of the Contact-Fatigue Wearing	eng
dc.type	ConferenceObject	cze
dc.description.abstract-translated	Railway steels are subjected to specific degradation mechanism due to combination of rolling contact loading and adhesive wearing. Precise evaluation of the surface layer's mechanical parameters is necessary for a service life prediction. Very low depth of localized dislocation hardening process doesn´t allow the standard mechanical testing. The operational degradation of surface layers due to a rolling contact process was simulated by a special testing rig. In the presented study, the rolling contact fatigue resistance of Hadfield steel was tested in two states – with and without explosive hardening. A specific limited state based on cumulative depletion of plasticity was achieved. Adhesive resistance of weld deposits was evaluated as an estimation of the operational durability of selected renovation technologies.	eng
dc.event	PROMATTEN 2016 (10.11.2016 - 11.11.2016)	cze
dc.peerreviewed	yes	cze
dc.publicationstatus	postprint	cze
dc.identifier.obd	39878042	cze